HiGlue PC 7227 Abrasion Resistant Coating- 2 Ib Kit
 |
|
| Materials |
Silicon Carbide& Epoxy |
| Model Number | PC 7227 |
| Appearance (Resin) | Grey |
| Appearance (Hardener) | Amber, Blue, Red, Yellow, Black...(Can Customize) |
| Resin Viscosity @ 25°C | 200,000~260,000 mPa.s |
| Hardnener Viscosity @ 25°C | 500~900 mPa.s |
| Mix Ratio, by weight (Resin:Hardener) | 4:1 |
| Shelf Life | 2 Years |
a. Inside of Chemical Process Tanks, Storage Tanks etc.
b. Pumps &Impeller, Valve Body.
c. Silo, Classifier &Ducts
d. Repairing of Glass Lined Vessels
e. Cooling Towers
f. Pipeline, shipping, Marine Applications
g. Propeller&Structures of marine industries.
h. Acid Proof Floor Coating
Surface Preparation: Proper surface preparation is critical to the long-term performance of this product. The exact requirements vary with the severity of the application, expected service life, and initial substrate conditions.
1. Clean, dry and abrade application surface. The more thorough the degree of surface preparation the better the performance of the application. If possible, it is recommended that the surface be grit blasted to a Near White Metal (SSPC-SP10/NACE No. 2) Standard. For less severe applications roughening the surface with hand tools is suitable.
2. Solvent cleaning with a residue-free solvent is recommended as the final step to aid in adhesion.
Mixing:
1. Material temperature should be between 20 °C to 30 °C.
2. Add hardener contents to resin. Mix material vigorously until uniform in color. Be sure to mix along the bottom and sides of mixing container. Mix three to five minutes.
Application Method:
1. Apply fully mixed material to the prepared surface. Caution: Use an approved, positive-pressure, supplied air respirator when welding or torch cutting near cured compound. Do Not use open flame on compound.