Abrasion-Resistant Coating Ceramic Epoxy Comes in Gray Ceramic-Reinforced Brushable Epoxy Coating

• Customization: Available
• CAS No.: 1344281
• Formula: Al2O3
• Model NO.: 7227
• EINECS: 215-691-6
• Bonding Function: Wearing Compound
• Morphology: Aluminum Powder Ceramic Particles Epoxy Paste
• Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing, Construction, Repairing Scrubbers, Ash Handling Sy
• Material: Epoxy
• Classification: Room Curing
• Main Agent Composition: Wearing Compound
• Characteristic: Wear Resistance
• Promoter Composition: Curing Agent
• Composition: Inorganic Material
• Color: Grey
• Transport Package: Carton
• Specification: 10kg
• Trademark: Higlue
• Origin: Jiangxi China
• HS Code: 3506100090
• Production Capacity: 20000PCS/Month
• Package Size: 10.00cm * 10.00cm * 10.00cm
• Package Gross Weight: 1.000kg

Product Description

China Direct Factory PC 7227 Grey Wearing Compound

 

Higlue PC 7227 Brushable Ceramic Wear Resistant Coating is a two-part, flowable, ultra-smooth, ceramic-reinforced epoxy that provides a high gloss, low friction coating, protecting equipment from corrosion and wear.

Higlue PC 7227 Brushable Ceramic Wear Resistant Coating is an ultra-smooth brushable, ceramic and silicon carbide filled, solvent-free coating that offers protection against turbulence, chemical attack, abrasion, and corrosion. The high gloss, low friction coating can be used to restore or increase pump efficiency. It can also be used to repair and protect heat exchanges and condensers, lining tanks, pipes, and chutes, resurfacing and repairing rudders and pintel housings and resurfacing cooling pump impellers and butterfly valves.

Ceramic Filled Epoxy/ Corrosion Repair Wearing Compounds

 

Ceramic beads filled epoxy repair putty is made up of high performance wear resistant and wear resistant ceramic particles and modified toughening and heat-resistant resin.

Ceramic beads wear resistant epoxy coating is widely used in repairing all kinds of wear parts and preparing wear-resistant and corrosion-resistant coatings on the surface of all kinds of machine parts. For example: repair and pre-protection of pipeline, elbow, mud pump, sand pump, centrifuge, packing box, slurry circulating pump body, impeller, size head of power plant desulfurization system, etc.

 


Features:

* Ceramic and silicon carbide-filled - to provide maximum protection
* Protects against abrasion, corrosion, and damage from turbulence
* Ultra-smooth brushable consistency
* Easy to mix and apply
* Reduces downtime
* Can be used as a topcoat over Wearing Compounds for applications requiring surface rebuilding and lasting protection

Ceramic Repair Putty

* Renews worn surfaces fast and reduces
* Downtime to put equipment back in service
* Quickly Easy to mix and use
* Non-sag paste allows application
* Versatility for overhead& vertical surfaces
* Non-shrinking
* Extends wear life
* Resists sliding abrasive wear
* Eliminates costly wear part
* Inventory Can be re-applied to
* itself Contains ceramic beads 1-1.5mm.

Technical Information

Name	HiGlue PC7227 Grey Brushable Ceramic
Appearance	Grey
Cure Time	24h @ 25 degree
Mix Ration(Weigth/ Volume)	4:1
Lap Shear Strength	24.2 N/mm2
Stee (grit blasted)	3500 psi

Product Type	Ceramic Repair Putty/ Abrasion Resistant Coating/ Wear Resistant Epoxy
Resistant Properties	Corrosion-Resistant
Pear Dia.	1- 1.5mm (can be customized)
Color	Grey (can be customized)
Mix Ratio by weight	8:1
Mix Ratio by volume	4:1
Working temperature	149ºC
Package Weight	30 lb per kit
working time	45-65 mins
Compressive strength(GB/T1041):	112.0MPa
Tensile strength(GB/T6329):	32.0MPa
Shear strength(GB/T7124):	14.0MPa
Flexural strength(GB/T9341):	45.0MPa
Fully curing time	16-24 hours
Shelf Life	12 month

 
Application

1. Cyclone and separator bodies
2. Dust collectors and exhausters
3. Pump liners and impellers
4. Fan blades and housings
5. Chutes and hoppers
6. Elbows and transition points


How to use
 

1. Surface treatment:
roughening the parts to be treated, sanding or sandblasting with an angle grinder, etc.; cleaning the roughened surface; the treated surface should be a rough and dry fresh substrate surface, and should be No oil and dust.

2. Preparation:
Mix the components A and B of the small particle wear-resistant protective agent according to the mass ratio A:B=2:1, and use them within 30 minutes.

3. Coating:
apply the uniformly mixed small particles of wear-resistant protective agent layer by layer to the area to be repaired, preferably at a thickness of 3-10 mm. The adhesive layer should be compacted to fully infiltrate the substrate; after the coating is applied to the required size, the surface layer is smoothed.

4. Curing:
Curing at 25ºC for 16 hours can be put into use. When the temperature is lower than 10 degrees, it can be cured by baking with an iodine tungsten lamp or electric heating plate for 2 hours.


Packing & Shipping 

500g/set, 5kg/set, 10kg/set, 13.7kg/set and 20kg/set
10kg/set carton size: 32x32x32.5

 

Our Company
CertificationFAQ

Q: Are you trading company or manufacturer ?A: We are factory which over 20 years of experience,and provide you direct prices.
Q: Can I be your agent?A: Sure, we are looking for agent all over the world.
Q: Do you provide samples ? is it free or extra ?A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: If I am not satisfied with the products ,when I get it,what should I do?A: If not satisfied it, please feel free to contact salesman soon, we will provide you the solution ASAP.

Can also be customized according to your requirements, welcome to contact us!