Repair and Pre-Protection of Pipeline, Impeller, Centrifuge, Pump Body 3kg 10kg High Temperature Ceramic Beads Wear Resistant Epoxy Coating

• Customization: Available
• Application: Automobile, Construction, Mining Repair
• Bonding Function: Structural Adhesive
• Model NO.: PC9313
• Color: Grey
• Composition: Organic Material
• Morphology: Paste
• Other Name: Ceramic Bead Epoxy Repair Putty
• Appearance(Resin): Grey (Can Customize)
• Appearance(Hardener): Dark Grey
• Appearanece(Mixed): Grey Paste
• Mix Ratio (by Weight Resin: Hardener): 2:1
• Cure: Room Tempetature Cure After Mixing
• Full Cure Time: 6h 12h 24h
• Temperature: -29 to +121 Degree
• Shelf Life: 1 Years
• Application-1: Slurry Pipelines, Tank Linings, Chutes Hoppers
• Application-2: Power Plant, Cement Dredge Pump Liners, Flumes.
• OEM/ODM: Yes
• Direct Factory: Yes
• Hot Sale Countries: South Africa, South America
• Deliver: in 20-30 Days
• Transport Package: Plastic Bucket
• Specification: 4kg 10kg 20kg
• Trademark: HiGlue
• Origin: China
• HS Code: 3506912000
• Production Capacity: 50000000piece Per Year
• Package Size: 32.00cm * 32.00cm * 32.00cm
• Package Gross Weight: 12.280kg
• Lead Time: 31 days (1 - 500 Sets) ; To be negotiated ( > 500 Sets)

Product Description

Product Description

High Impact Wear Resistant Mining Machine Coatings Epoxy Adhesives 

High-alumina, ceramic bead-filled epoxy system for outstanding abrasion resistance to processing equipment.

Ceramic beads filled epoxy repair putty is made up of high performance wear resistant and wear resistant ceramic particles and modified toughening and heat-resistant resin. 

Ceramic beads wear resistant epoxy coating is widely used in repairing all kinds of wear parts and preparing wear-resistant and corrosion-resistant coatings on the surface of all kinds of machine parts.

For example: repair and pre-protection of  lining and protecting flumes, troughs, elbows, hoppers, discharge chutes, and other processing equipment,desulfurization system, etc.

Specification

Product Name	PC9313/ PC11490
Ratio by weight	A:B=2:1
Curing Time	30 mins/ 6hr
Temperature	-29°C~+121°C
Shelf life	1 years
Feature	Impact Resistan, Renews worn surfaces, Non shrinkage, wear resistant
Hardness (shore D)	85
Compressive Strength	83 N/mm2

How To Use

1. Cleaning:Remove dirt, oil, grease, loose flanky rust etc., with a suitable high pressure water cleaning system . 

2. Blasting:Blast all surfaces to be coated, with a sharp edged angular grit, such as aluminum oxide, to a depth of profile of approximately 75 microns and a degree of cleaniness of very thorough Blast Claeaning/Near Whitef.

3. Cleaning:After blasting metal surfaces should be cleaned with a waterless or solvent, and allow the surface to dry before application of the product coat the surface before any oxidation or contamination takes place.

4. Protection From Flash Rusting:To avoid flash rust,repairs should be made as soon as possible or within a mixmum 2 hours of blasting.

5. Mixing The Material:Measure 2 parts resin to 1 part hardener by volume or weight if doing a partial kit. Otherwise, mixing a full kit is pre-measured at the correct ratio. For a full kit mix, a spiral mixing blade attached to a high torque electric or pneumatic drill can be used. For a partial kit transfer measured quantities onto a clean and dry mixing surface to mix together witha trowel until uniform in color. If resin and hardener temperatures are 15ºC or below, preheat resin only, to about 30ºC but not to exceed 40ºC.

6. Application:Apply fully mixed material to the prepared surface. Initially apply the material in a very thin layer to "wet" out the surface and ensure full epoxy contact with the roughened surface. Build up to desired thickness(minimum 6 mm), avoiding air entrapment. At 25ºC,the working time is 15 minutes and functional cure time is 4 hours Working and cure time depend on temperature and mass the higher the temperature and the larger the mass, the faster the cure.

Application